There is provided a method for preparing a highly accelerated-phosphorescent phosphor whose erasability and after-image characteristic are both improved. Phosphor materials are mixed together to obtain a mixture, and the mixture of phosphor materials is fired in a furnace having a firing region whose capacity is 2 to 500 L per kilogram of the mixture, at a temperature of 550 to 1000 DEG C while introducing 1 to 200 ml of oxygen in volume at room temperature per liter capacity of the firing region in the furnace, to thereby prepare a phosphor represented by the following compositional formula (I) : (Ba1-a, Ma) FX . bM . cM . dA : xLn wherein, Ma is alkaline earth metal such as Sr, Ca or Mg; M is alkali metal such as Li, Na or K; M is Al, Ga or In; X is Cl, Br or I; Ln is rare earth element such as Ce, Eu or the like; A is a metallic oxide such as Al2O3; and a, b, c, d and x are numerical values within the ranges of 0
|